Min. Order: 1ton
metal abrasive
Steel cut wire shot
Steel cut wire shot production standards:
We strictly according to American motorcar engineer association "J441 SAE standards," the People's Republic of China machinery industry "JB/T 8354-1996 steel wire cut shots standard" material requirements to production, but since using recycled steel wire its length and standard a slightly different.

The specification of steel cut wire shot:
1.0mm, 1.5mm, 2.0mm,2.5mm
Steel grit, with its main technical indices:

Product Steel cut wire shot


Chemical composition （C） 0.45~0.85%
0.3~1.30%
0.15～0.35%
≤0.05%
≤ 0.04%
（Mn）
（Ｓi）
（S）
（P）
Average hardness
(500g load were determined under) 1.0mm：51～53 HRC(525～561HV)
1.5mm：41～45 HRC(388～436HV)
Hardness deviation Maximum deviation range ±3.0HRC or ±40HV
Microstructure
Longitudinal (Deformed Pearlite)
horizontally (Deformed Pearlite)
Density 7.8/cm3













Steel cut wire shot of application:
Steel wire cut blast cleaning: peen-forming cleaning, body.they, die casting cleaning, casting peen-forming cleaning, forgings peen-forming cleaning, forgings body.they casting oxidized workpieces
Steel cleaning, steel plate cleaning, cleaning, h-beam cleaning, steel structure cleaning.
Steel cut wire shot derusting: peen-forming derusting, shot peening derusting, casting derusting, forging steel derusting, forging except rust oxide skin, steel derusting, h-beam derusting
Steel structure rust.
Steel wire cut pill strengthen: peen-forming aggrandizement, heat-treated pieces shot peening, gear shot peening.
Steel cut wire shot shot peening: steel shot peening, sections of sandblasting, presented.the peen-forming, steel plates, steel shot peening shot peening.
Steel cut wire shot peen-forming: plate peen-forming, steel shot bla, sections peen-forming.
Steel cut wire shot dozen sand: play sand treatment.
Steel cut wire shot before treatment: before painting processing, coating pretreatment, surface pretreatment, presented.the pretreatment, steel pretreatment, steel pretreatment, steel beforehand
Processing, steel structure pretreatment.